Case CRAWLER DOZER 650L TIER3 - Consumables Loctite Product Chart

INTRODUCTION
ConsumablesLoctite®ProductChart
BondingAdhesives
Prod-
uct
ColorStrengthFixture/Full
Cure(Steel/
Steel)Time
Recom-
mended
Primeror
Activator
Description
312
Clear
9.8-17.2MPa
(1421-2495
psi)
2min/24hrs
736Typicalapplicationsincludebondingdissimilar
materialssuchasmetals,glassorceramicsand
wherefastxturingisrequiredbetweenclosetting
parts.
324Light
amber
34-614MPa
(4932-89061
psi)
30min/24hrs
7075
Isusedtobondatpartstogether.Especially
suitableforjoiningdissimilarmaterials,e.g.ferrite
toplatedmaterialsinelectricmotors,loudspeakers,
etc.Thisproductisspecicallyformulatedfor
toughnessandimpactstrength.
326Yellow
tolight
amber
34-300MPa
(4932-43515
psi)
3min/6hrs
7649
onone
surface
Typicalapplicationsincludebondingferritesto
platedmaterialsinelectricmotors,loudspeaker
hardwareandjewelrywherefastxturingis
required.
380Black
26MPa(3770
psi)
2min/24hrs
none
Isarubbertoughenedadhesivewithincreased
exibilityandpeelstrengthalongwithenhanced
resistancetoshock.
409
Clear
to
slightly
cloudy
18-26MPa
(2611-3771
psi)
2min/24hrs
none
Isageneralpurposecyanoacrylateadhesivegel.
Thegelconsistencypreventsadhesiveoweven
onverticalsurfaces.
426Black4.8-20.7MPa
(696-3003psi)
10sec/40sec.
none
Isanadhesivegeltoughenedwithelastomers
forimpactandpeelstrengthalongwithimproved
resistancetoheatandhumidity.
454
Clear
to
slightly
cloudy
19-28MPa
(2756-4061
psi)
1min/72hrs
none
Isparticularlysuitedforbondingporousor
absorbentmaterialssuchaswood,paper,leather
andfabric.
455
Clear
tolight
yellow
9.7MPa(1407
psi)
30sec/24hrs
none
Isageneralpurposecyanoacrylateadhesivegel
withlowodorandlowbloomingpropertiesandis
particularlysuitableforapplicationswherevapor
controlisdifcult.
480Black22-30MPa
(3191-4352
psi)
2min/24hrs
none
Isarubbertoughenedadhesivewithincreased
exibilityandpeelstrengthalongwithenhanced
resistancetoshock.
495
Clear
to
straw
colored
12-26MPa
(1741-3771
psi)
10sec/30sec.
none
Isageneralpurposecyanoacrylateinstant
adhesive.
E60HPPale
yellow
29.8MPa(4322
psi)
3hrs/24hrs
none
Isatoughened,mediumviscosity,industrialgrade
epoxyadhesivewithextendedworklife.Once
mixed,thetwo-componentepoxycuresatroom
temperaturetoformatough,off-white,bondline
whichprovideshighpeelresistanceandhighshear
strengths.Thefullycuredepoxyisresistanttoa
widerangeofchemicalsandsolvents,andactsas
anexcellentelectricalinsulator.