ZUCCHETTI KOS - TECHNICAL DATA SHEET; DENSITY; TENSILE STRENGTH; ULTIMATE STRENGTH

24
PROPRIETÀ
PROPERTIES
EIGENSCHAFTEN
PROPRIETES
PROPIEDADES
RISULTATI
RESULTS
ERGEBNISSE
RESULTATS
RESULTADOS
UNITÀ DI MISURA
UNIT OF MEASURE
MASSEINHEITEN
UNITE DE MESURE
UNIDAD DE
MEDIDA
METODO
METHOD
METHODE
METHODE
METODO
DENSITÀ
DENSITY
DICHTE
DENSITE
DENSIDAD
1.7-2.00 g/cm
3
METODO INTERNO
INTERNAL METHOD
INNERES VERFAHREN
METHODE INTERNE
METODO INTERNO
ASSORBIMENTO D’ACQUA DOPO 48 ORE
WATER ABSORPTION AFTER 48 HOURS
WASSEREINNAHME NACH 48 STUNDE
ABSORPTION D’EAU APRES 48 HEURES
ABSORCION DEL AGUA DESPUES DE 48 HORAS
<0.3%UNI EN 62:2001
DUREZZA BARCOL
BARCOL HARDNESS
BARCOL-HÄRTE
DURETE BARCOL
DURETE BARCOL
65
° scala Barcol
° Barcol scale
° Barcol scale
° échelle Barcol
° escala Barcol
ASTM D 2583-81
RESISTENZA A FLESSIONE
TENSILE STRENGTH
ZUGFESTIGKEIT
RESISTANCE A LA FLEXION
RESISTENCIA A LA FLEXIÓN
32.30MPa EN ISO 178:2003
RESISTENZA A FLESSIONE – MODULO DI ELASTICITÀ
TENSILE STRENGTH – YOUNG’S MODULUS
ZUGFESTIGKEIT – ELASTIZITÄTSMODUL
RESISTANCE A LA FLEXION – MODULE D’ELASTICITE
RESISTENCIA A LA FLEXIÓN – MÓDULO DE
ELASTICIDAD
9102MPa EN ISO 178:2003
RESISTENZA A TRAZIONE
ULTIMATE STRENGTH
BRUCHFESTIGKEIT
RESISTANCE A LA TRACTION
RESISTENCIA A LA TRACCIÓN
19.80MPa EN ISO 527:1996
RESISTENZA A TRAZIONE – ALLUNGAMENTO A
ROTTURA
ULTIMATE STRENGTH – ELONGATION AT BREAK
BRUCHFESTIGKEIT – REISSLÄNGE
RESISTANCE A LA TRACTION – ALLONGEMENT A LA
RUPTURE
RESISTENCIA A LA TRACCIÓN – ALARGAMIENTO A LA
ROTURA
0.26 % EN ISO 527:1996