beasleep whilethe glasscoolsand they won’tbetempted to
open the door.
After each firing, examine the shelf. Recoat if the kiln
washischipped.Whenglassstickstoabaresectionofshelf,
the glass cracks.
Glass Bubbles
Probable Causes:
I
Heating the Kiln Too Fast
I
Air Trapped Between Layers of Glass
I
Grease or Dirt Between Layers of Glass
I
Uneven Glass Volume
I
Moisture or trapped Air Between the Glass and Shelf
Makesuretheshelfiscompletelydrybeforefiring.If you
have applied freshglass separator, leavethe shelf inthe kiln
at 300°F/148°C for 20 minutes before placing glass on it.
One way to eliminate bubbles is to hold the temperature
at 100°F/55°C below fusing temperature for 15 minutes.
This gives the shelf time to heat up to match the tempera
-
ture of the glass.
Glass Devitrification (Frosty Surface)
Probable Causes:
I
Impurities in Glass
I
Kiln Not Vented Long Enough During Initial Heating
Devitrification is a frosty surface on the glass caused by
impurities. With some glasses, it is unavoidable. To lessen
devitrification, some artistsvent thedoor ofthe kiln slightly
afterfusingiscompleted.Theyclosethedoorwhentheglass
reaches 1000°F/537°C.
Glass Separator Sticks To Glass
Probable Causes:
I
Firing Too Hot
I
Overglaze On the Back of the Piece
Instead of firing to a full fuse temperature, try firing
50°F/28°Ccoolerandholdingatthattemperatureforseveral
minutes.
Ceramic Overglaze
Breaking in Overglaze Firing
Canbecausedbypoorlyfiredbisque.Aslowbisquefireis
always better for ware that is to be china painted. The
greenware should be completely dry before being placed in
the kiln.
Purple Spots in Gold
Usuallyduetoathinapplicationofgoldortoomuchthin
-
ner.Ifgoldisappliedaccidentallytoanareaitwillshowpur
-
ple after being fired unless cleaned with a good gold re
-
mover.
Broken Lines in Gold
Can be caused by overfiring or too heavy an application.
However, this can be very attractive when gold is crackled
over a dark color of fired glaze.
Peeling China Paint
Can be caused by the paint being applied too heavily.
Loss of Color in China Paints
Usually a result of overfiring or thinning your paint with
too much medium when applying.
Faded Colors in Overglaze Decals
This is the result of either underfiring or overfiring. If
pinks and reds are drab, refire to a hotter cone. When used
withachinapaintbackground,applyandfirethedecalsfirst,
thenchinapaintandfireagain.Checktherecommendations
ofdecalsupplier.Ifdecalwasunderfired,refiretoproperfir-
ingcone. Ifdecalwasoverfired,the designmayberepainted
in china paints and refired.
Weakening of Luster Colors
This can be caused by overfiring.
White Spots in Lusters or Metals
Can be caused by moisture on the ware before it was
placedin thekilnorfrom havingbeenfiredatthesametime
as other overglazes.
Note: Apply lusters only on a dry day.
Powdering of Luster Colors
This can be caused by too heavy an application.