Zircon Master S En 230V v11 3
The cleaning program in the furnace is recorded as
program №01 CLEAN.
After preparing the furnace for operation, run program
CLEAN at least three times. Never sinter immediately
after installing the heaters!
Further, as you begin the real work, do not put a lot of
sintering material in the chamber. Do not treat your
teeth with liquid stains!
Alternate to performing a normal and clean cycle
(program №01 CLEAN) at least the first 30 times.
Do not use water-based zirconium dyes for pre-dyeing
before doing 30 sintering cycles. The first step is to build
a glass-like protective layer on the heaters (See Figure 1).
Otherwise, steam from the dyes will oxidize the
molybdenum in the heaters and will damage or destroy
them.
When you start to use water-based dyes for pre-coloring
zirconium, it is MANDATORY to follow the instructions for
use with dyes that manufacturers prescribe.
Drying the cut and dyeing elements is EXTREMELY
IMPORTANT for the good condition of the heaters and
the furnace. Failure to do so will cause damage or
destruction of the heaters - see the SCHUPP brochure.
The use of non-water based zirconium dyes is highly
undesirable. This can result in the destruction of the
heaters and the contamination of the furnace chamber.
WARNING!
Failure to follow the instructions for initial
furnace operation can result in destruction
of the heaters and compromise the end
result of your work!
Example procedure for initial furnace operation:
1. 1. Do three (3) cycles with program №01 CLEAN
with empty chamber (no sintering material)
2. Start normal furnace operation. Alternate a
sintering cycle (your program according to the
instructions of the zirconium manufacturer you
have chosen) and a cycle with program # 01
CLEAN. This cycle rotation should be at least 30
times.
3. After each cycle, evaluate the condition of the
heaters.
4. Strictly follow the instructions for the quantity
and type of sintering material. Do not stain
zirconium in advancе.
5. Also use NACERA powder for each sintering
cycle with sintering material.
To Next Page