Questions and Answers:

R
Rachel ThomasAug 1, 2025
Why is there excessive spatter when using my Eastwood Mig135 Welding System?
- A
  Allison MartinezAug 1, 2025
  Excessive spatter can occur due to several factors. You might have the wire speed set too fast; try adjusting it to a slower setting. Ensure the base metal is clean by removing any paint, rust, oil, grease, dirt, or contaminants from the surface. Check that you're using the correct shielding gas (75% Argon / 25% CO2) and increase the flow rate, being mindful of any crosswinds. Verify that the welding wire is appropriate for the material and process. Also, make sure the contact tip on the welding gun is closer to the workpiece to shorten the exposed welding wire.
M
Michael DixonAug 5, 2025
What to do if my Eastwood Mig135 has burn through?
- W
  whitecarolAug 5, 2025
  If you're experiencing burn through, it could be due to high voltage. Try adjusting the voltage output to a lower setting. Also, check the wire speed; if it's too fast, adjust it to a slower setting. Finally, make sure you aren't moving the welding gun too slowly; increase your travel speed.
D
david81Aug 9, 2025
Why Eastwood Mig135 Welding System has porosity?
- C
  cdrakeAug 9, 2025
  Porosity can be caused by several factors. Ensure you have adequate shielding gas flow and watch out for crosswinds that might disrupt it. Verify you're using the correct shielding gas mixture (75% Argon / 25% CO2). Also, make sure to thoroughly clean the base metal to remove any paint, rust, oil, grease, dirt, or other contaminants. Finally, check that the contact tip on the welding gun is close enough to the workpiece to minimize exposed welding wire.
B
Bryan SolisAug 14, 2025
How to fix lack of penetration with Eastwood Mig135?
- C
  castillosophiaAug 14, 2025
  Lack of penetration can occur for several reasons. Try adjusting the voltage to a higher setting and increasing the wire speed. Slow down your travel speed with the welding gun, making sure to pull or drag the molten metal puddle. Ensure the contact tip is close to the workpiece to shorten the length of exposed welding wire. Keep in mind that the MIG135 is rated for a maximum thickness of 1/4"; exceeding this will result in poor penetration. If welding heavy gauge metals, increase the welding gap and bevel the edges on the weld side of the pieces.
B
Brian RodriguezAug 18, 2025
What causes warping with my Eastwood Mig135 Welding System?
- E
  Elijah JonesAug 18, 2025
  Warping can be caused by a lack of tack welds; make sure to tack weld the pieces in multiple areas to prevent them from pulling apart. Ensure you're using welding clamps to secure the pieces in their proper shape. To prevent warping, allow the piece to cool after welding small sections at a time, spreading out the heat.
M
margaret34Aug 23, 2025
Why Eastwood Welding System has poor fusion?
- D
  Dr. Michael FrenchAug 23, 2025
  Poor fusion can be caused by several factors. Try adjusting the voltage output to a higher setting and increasing the wire speed. Ensure the base metal is clean by removing any paint, rust, oil, grease, dirt, or any other contaminants. Also, make sure the contact tip on the welding gun is closer to the workpiece to shorten the length of exposed welding wire. If welding a large piece, preheat your part with a torch.
K
kristen77Aug 27, 2025
What causes excessive penetration with my Eastwood Mig135?
- T
  Terri Boyer DVMAug 27, 2025
  Excessive penetration might be due to high voltage. Adjust the voltage to a lower setting. The wire speed may be too fast, so adjust it to a slower setting. Also, check the travel speed of the welding gun; if it's too slow, increase it.