+GF+ SG 160 - Page 45

Operating instructions SG 160 9 Fusion data
41
S 8
SDR 17
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
1.9
2,4
3,0
3.8
4.5
5.4
6.
6
7.4
8.3
9.5
A: Fusion surface
mm²
180
283
443
707
997
1435
2144
2734
3434
4491
F1&F5 : fusion force
daN
3
4
7
11
15
22
32
41
52
67
Bead
mm
0.5
0.5
0.5
0.5
0.5
1.0
1.0
1.5
1.5
1.5
F2: heating force
daN
1
1
1
1
1
1
2
3
3
4
t2: heating time
sec
45
24
30
38
45
54
66
74
83
95
t3: change over time
sec
5
5
5
5
5
5
6
6
6
7
t4: Pressure buildup time
sec
5
5
5
5
5
5
6
6
6
7
t5: Cooling time
min
6
6
6
6
6
7
9
10
12
13
S 6.3
SDR 13.6
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
2.
4
3,0
3,7
4.7
5.6
6.7
8.1
9.2
10.3
11.8
A: Fusion surface
mm²
223
349
538
861
1221
1753
2593
3347
4197
5494
F1&F5 : fusion force
daN
3
5
8
13
18
26
39
50
63
82
Bead
mm
0.5
0.5
0.5
1.0
1.0
1.0
1.5
1.5
1.5
1.5
F2: heating force
daN
1
1
1
1
1
2
3
3
4
5
t2: heating time
sec
45
30
37
47
56
67
81
92
103
118
t3: change over time
sec
5
5
5
5
5
6
6
6
7
8
t4: Pressure buildup time
sec
5
5
5
5
5
6
6
6
7
8
t5: Cooling time
min
6
6
6
6
8
10
11
13
14
16
S 5
SDR 11
Ø
32
40
50
63
75
90
110
125
140
16
0
e: wall thickness
mm
2.9
3.7
4.6
5.8
6.8
8.2
10.0
11.4
12.7
14.6
A: Fusion surface
mm²
265
422
656
1042
1457
2107
3141
4068
5078
6669
F1&F5 : fusion force
daN
4
6
10
16
22
32
47
61
76
100
Bead
mm
0.5
0.5
1.0
1.0
1.0
1.5
1.5
1.5
2.0
2.0
F2: hea
ting force
daN
1
1
1
1
1
2
3
4
5
7
t2: heating time
sec
45
37
46
58
68
82
100
114
127
146
t3: change over time
sec
5
5
5
5
6
6
7
8
8
8
t4: Pressure buildup time
sec
5
5
5
5
6
6
7
8
8
9
t5: Cooling time
min
6
6
6
8
10
11
14
16
17
19
S 4
SDR 9
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
3.6
4.5
5.6
7.1
8.4
10.1
12.3
14.0
15.7
17.9
A: Fusion surface
mm²
321
502
781
1247
1757
2535
3775
4882
6130
7990
F1&F5 : fusion force
daN
5
8
12
19
26
38
57
73
92
120
Bead
mm
0.5
0.5
1.0
1.
5
1.5
1.5
2.0
2.0
2.0
2.0
F2: heating force
daN
1
1
1
1
2
3
4
5
6
8
t2: heating time
sec
45
45
56
71
84
101
123
140
157
179
t3: change over time
sec
5
5
5
6
6
7
8
8
9
10
t4: Pressure buildup time
sec
5
6
6
6
6
7
8
9
10
11
t5: Cooling time
min
6
6
8
10
12
14
16
18
20
22