+GF+ SG 160 - Page 52

9 Fusion data Operating instructions SG 160
48
Ø Outside pipe diameter
e Wall thickness
A Fusion surface
F1 Equalization force
F2 Heating force
F5 Fusion force
PN 16
Ø
32 40 50 63 75 90 110 125 140 160
e: wall thickness
mm
–
–
3,0 3,0 3,6 4,3 5,3 6,0 6,7 7,7
A: Fusion surface
mm²
–
–
443 565 808 1158 1743 2243 2806 3684
F1&F5 : fusion force
daN
– –
4 6 8 12 17 22 28 37
Bead / Wulst / Bordino
mm
– –
0,5 0,5 0,5 0,5 0,5 0,5 0,5 0,5
F2: heating
force
daN
– –
1 1 1 1 2 2 3 4
t2: heating time
sec
– –
70 70 76 83 93 100 107 117
t3: change over time
sec
– –
3 3 3 3 3 4 4 4
t4: Pressure buildup time
sec
– –
4 4 5 5 5 6 6 6
t5: Cooling time
min
– –
6 6 6 7 8 9 10 11
PN 10
Ø
32 40 50 63 75 90 110 125 140 160
e: wall thickness
mm
– – –
2,0 2,3 2,8 3,4 3,9 4,3 4,9
A: Fusion surface
mm²
– – –
383 525 767 1139 1484 1833 2388
F1&F5 : fusion force
daN
– – –
4 5 8 11 15 18 24
Bead / Wulst / Bordino
mm
– – – 0.5 0.5 0.5 0.5 0.5 0.5 0.5
F2:
heating force
daN
– – –
1 1 1 1 1 2 2
t2: heating time
sec
– – –
60 63 68 74 79 83 89
t3: change over time
sec
– – –
3 3 3 3 3 3 3
t4: Pressure buildup time
sec
– – –
4 4 4 4 5 5 5
t5: Cooling time
min
– – –
5 5 6 6 6 7 8
PN 2.5
Ø
32 40 50 63 75 90 110 125 140 160
e: wall thickness
mm
– – –
2,5 3,0
–
3,0
–
3,0 3,0
A: Fusion surface
mm²
– – –
475 679
–
1008
–
1291 1480
F1&F5 : fusion force
daN
– – – 5 7 – 10 – 13 15
Bead / Wulst / Bordino
mm
– – – 0.5 0.5 – 0.5 – 0.5 0.5
F2: heating for
ce
daN
– – – 1 1 – 1 – 1 1
t2: heating time
sec
– – – 65 70 – 70 – 70 70
t3: change over time
sec
– – – 3 3 – 3 – 3 3
t4: Pressure buildup time
sec
– – – 4 4 – 4 – 4 4
t5: Cooling time
min
– – – 5 6 – 6 – 6 6