Table 5. Chemical Durability
Reagent Time Temperature (ºC)
Weight Loss (mg/cm2)
HCl - 5% 24 hrs 95 5.9
NH4F:HF - 10% 20 min 20 1.0
HF - 10% 20 min 20 25.2
NaOH - 5% 6 hrs 95 2.7
Electrical
Table 6. Electrical
Frequency (MHz) Dielectric Constant Loss Tangent
54 7.08 0.009
163 7.01 0.010
272 7.01 0.011
272 7.00 0.010
490 7.99 0.010
599 7.97 0.011
912 7.01 0.012
1499 6.99 0.012
1977 6.97 0.014
2466 6.96 0.014
2986 6.96 0.014
Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and 1355-R
Putting Corning Gorilla Glass 5 to the test.
• Greater damage resistance (upto 1.8X) with deep abrasion.
• Faster chemical strengthening with high Compressive Stress and deeper depth of compression
• Shallower check depth with higher abrasions levels
• Enables thickness reduction