The HotStart pulse cycles can be corrected with the following filler metals:
-
AlMg 4.5 Mn / 100 % Ar / 1.2 mm (CMT 0874)
1)
- AlSi 5 / 100% Ar / 1.2 mm
- CrNi 19 9 / Ar + 2.5 % CO2 / 0.8 mm
- CrNi 19 9 / Ar + 2.5 % CO2 / 1.0 mm
- CuAl 5 Ni 2 / 100 % Ar / 1.0 mm
Pulse correction
for continuous correction of the droplet detachment energy
-5 lower droplet detachment force
0 neutral droplet detachment force
+5 higher droplet detachment force
The pulse can be corrected with the following filler metals:
-
AlMg 4.5 Mn / 100% Ar / 1.2 mm
2)
-
AlSi 5 / 100 % Ar / 1.2 mm (CMT 0880)
2) 3)
-
AlSi 5 / 100 % Ar / 1.2 mm (CMT 0881)
2) 4)
-
CrNi 19 9 / Ar + 2.5 % CO2 / 0.8 mm
2)
-
CrNi 19 9 / Ar + 2.5 % CO2 / 1.0 mm
2)
-
CrNi 19 9 / Ar + 2.5 % CO2 / 1.2 mm
2)
-
CuAl 8 / 100 % Ar / 1.0 mm
2)
-
CuSi 3 / 100 % Ar / 1.0 mm
2)
Notes
1)
Different ignition process from the CMT 0875 characteristic
2)
Combination of CMT characteristic and pulse characteristic
3)
CMT/pulse characteristic with more pulse cycles than CMT cycles
4)
CMT/pulse characteristic with fewer pulse cycles than CMT cycles
Gas pre-flow time
Gas post-flow time
Feeder creep speed
The settings for the background parameters gas pre-flow time, gas post-flow time and
feeder creep speed are described in the Setup menu.
Adjusting para-
meters for cor-
rection
1
Press the Parameter selection button to select the parameter you wish to correct
2
Use the adjusting dial to set the selected parameter to the desired value. The para-
meter value is displayed in the digital display located above it.
110