Criteria Standard Property, characteristic value Unit
Additives -
● Anti-Oxidation (AO), Anti-Wear (AW)
● No solid lubricants
● Alternatively: Extreme-pressure (EP) only after
prior consultation with grease and bearing
manufacturers
-
FE9 test: A/1500/6000 DIN 51821-1/-2 F10 ≥50 h at +130 °C
F50 ≥100 h at +130 °C
H
Behavior in the presence of water DIN 51807 0 or 1 at a test temperature of +90° C -
Corrosive effect on copper DIN 51811 0 or 1 at a test temperature of +120° C Korr.°
Corrosion resistance (EMCOR) DIN 51802 /
ISO 11007
0 - 0 Korr.°
Solid matter content, particle sizes >
25 µm
DIN 51813 <10 mg/kg mg/kg
Suitability of bearings
Speed parameter nxdm
- Suitable for the built-in motor bearings, seals and
these speeds
-
mm/min
Note
Deviating operating conditions and characteristics
Only use the grease type that is specified on the lubricant plate.
● If the operating conditions differ from those mentioned, other greases may only be used
after prior consultation with the manufacturer.
Note
Use of other greases
If greases other than those named on the lubricant plate are used, it cannot be guaranteed
that they are compatible with the complete system.
● If you use greases that satisfy only the minimum requirements of DIN 51825 or ISO 6743-9,
then reduce the lubrication intervals by half or adapt them as appropriate.
● If in doubt, consult the manufacturer.
Recommended greases for roller bearings
For standard applications, the following high-quality greases are recommended for roller
bearings for vertical and horizontal motor constructions due to their technical properties:
Table 9-2 Roller bearing greases for vertical and horizontal types of construction
Manufacturer Grease type
Shell Gadus S2 V100 3
ExxonMobil Unirex N3
Esso
BP Energrease LS3
Fuchs Renolit H443 HD88
Lubcon Turmoplex 3