enCoating Specifications for Underwater Components Made of SteelMIX−Fr 109807108/18332/3
Observe before applying final coat:
D Rust should be manually removed (ST 3) from shipping and assembly damage according to DIN 55928.
D Use the material listed above and retouch the primer to the specified layer thickness.
NOTE
Before applying the final coat, thoroughly clean parts with HAKU 1025-800 cold degreaser (KLUTHE/ID
no. 1017753), leaving no residue.
Then rinse off the cleaned parts using fresh water.
Always observe applicable technical bulletins and safety data sheets.
When retouching damage to the coating system, ensure that individuals layers are structured the same as intact
surfaces. The HEMPEL system can be used without any modifications as a repair coat on the old KZA or EGA
system, etc.
Final Coat (3 Layers)
Material Dry-film thickness ID no.
1st
HEMPADUR 4514A, black (19990), 2-component cured
epoxy paint*
80 - 100 mm
1140424
or
INTERSHIELD KZA 352, black, 2-component cured epoxy
paint
80 - 100 mm
1087070
2nd
HEMPADUR 4514A, reddish brown (50630), 2-component
cured epoxy paint*
80 - 100 mm
1140425
or
INTERSHIELD KZA 351, red, 2-component cured epoxy
paint
80 - 100 mm
1087069
3rd
HEMPADUR 4514A, black (19990), 2-component cured
epoxy paint*
80 - 100 mm
1140424
or
INTERSHIELD KZA 352, black, 2-component cured epoxy
paint
80 - 100 mm
1087070
* To be used with curing agent 97430 (ID no. 1140426)
Layer thick-
ness
[micron]
Theoretical
spreading rate
Methods of application
Product name
(incl. grade
number)
Sur-
face
[%]
Colour Colour
no.
Wet Dry [m
2
/l] Brush Air-
less
Recom-
mended
nozzle ori-
fice
Recom-
mended
nozzle
pressure
[bar]
HEMPADUR
4514A
F/C Black 19990 200 125 4.8 (X) X .019”-
.023”
250
HEMPADUR
4514A
F/C Reddish
brown
50630 200 125 4.8 (X) X .019”-
.023”
250
HEMPADUR
4514A
F/C Black 19990 200 125 4.8 (X) X .019”-
.023”
250
T/U: Touch-up
F/C: Full coat
DLT: Dry-layer
thickness
375 X: Preferred (X): Possible
To Next Page